The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0-10.5 mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Set cross-cut adhesion, film thickness and Buchholz Crowd Hardness three test functions in one, cross-cut knife 6 blade spacing 1mm/2mm, Crowd knife load 500 +/- 5g, using the destruction Measurement principle.
Made of stainless steel, the cutter tooth spacing is 1-3mm, the cut mark length is 35mm, and the coating is cut through the grid pattern, and the adhesion effect is evaluated according to the six-level classification, which is suitable for a variety of surface tests.
The device adopts destructive measurement, resolution +/- 0.001mm, can carry out V-shaped incision, grid cutting and Cedar test, directly observe Coating thickness and Cedar length, support multi-layer film analysis.
Hydraulic system measurement coating adhesion, accuracy control within +/- 1% full scale, optional 10mm to 50mm more than the kit size, self-positioning characteristics to ensure smooth rough surface measurement results accurate and reliable.
Rotation speed 80rpm, Working Travel 80mm, in line with international standards, to ensure accurate and reliable film adhesion assessment.
Tack is good and non-degumming, adhesion reaches 7.6 N/cm, mass performance is stable, suitable for cross-cut adhesion testing, to ensure accurate film integrity assessment.
Hydraulic system measurement coating adhesion, accuracy control within +/- 1% full scale, equipped with multi-function digital display, can automatically calculate different kit size results, self-positioning kit to adapt to various surfaces.
Equipped with three swirl/spin cutter heads, the tooth spacing is 1mm, 2mm and 3mm respectively, and it is designed according to ISO2409 standard for accurate evaluation of coating adhesion performance.
Adopt the circular roller scratch method to evaluate the adhesion grade, describe the adjustable diaMeter of 0-10.5 mm, equipped with four weights to achieve 200-1000g loading, table Travel ≥ 80mm, manual operation is stable and reliable.
The adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel ≥ 80mm. The integrity of the paint film was evaluated by seven grades, and the operation was simple and conformed to the GB/T1720 standard.
Hydraulic system to achieve coating detachment test, accuracy of +/- 1% full scale, equipped with multi-function digital display, support for a variety of kit size automatic calculation, portable design for a variety of places.
Hydraulic system measurement coating adhesion, accuracy control within +/- 1%, equipped with self-positioning kit to ensure smooth and rough surface measurement results consistent, optional 10mm to 50mm variety of kit specifications.
35Mm cross-cut length and 1mm pitch design, stainless steel material to ensure dimensional accuracy, equipped with tape and brush for film adhesion testing.