The tapered shaft size range is 3.2~ 38mm, and the shaft length is 203mm, which can test the cracking and disbonding performance of the paint film under bending conditions, in line with international standards.
Using pure mechanical design, the coating performance is measured by conical mandrel bending test plate, the test plate size is 100mm × 180mm, the thickness is less than or equal to 0.8mm, and the operation is simple and reliable.
The cone shaft is used to test the anti-cracking performance of coatings with different curvatures. The size of the cone shaft is Φ 3.1~ 38mm, the volume is small and the weight is light, which is convenient for laboratory and field use.
Tapered shaft size Φ 3.1~ 38mm, shaft Rod size 2-32mm, anodic oxidation aluminum and stainless steel material, ergonomic design clamping device, bending arm large knob for easy operation, suitable for measuring plate thickness ≤ 0.8mm.
Using conical mandrel design, can measure the cracking resistance and elongation of the coating, the thickness of the test plate supports 0.8mm, easy to operate without power supply, to meet a variety of standard test requirements.
Using 12 stainless steel shaft Rods with a diaMeter of 2-32mm, the 50mm wide test plate can be tested for 180 ° bending. The coating cracking situation is detected by decreasing the diaMeter of the shaft Rod, and the operation is simple and fast.
The conical mandrel bending range is 3.1 to 38mm, and the plate thickness can be tested by 0.8mm. The panel is instantly locked and unlocked with a fast lever handle, which is convenient for operation.
With a conical mandrel design, the resilience of the coating can be evaluated in a single test in the diaMeter range of 3.1 to 38mm, and the thickness of the test plate is less than or equal to 0.8mm.
Equipped with 8 kinds of diaMeter shaft Rods from 2 to 12mm, the 180 degree bending test can be completed in 1-3 seconds, and the anti-cracking performance of the paint film can be evaluated with the smallest shaft Rod diaMeter, which is easy to operate.
The cone shaft length is 203mm and the large end diaMeter is 38mm, which can test the cone bending resistance of a single layer or the entire coating system separately. Operating temperature is 23 +/- 2 ℃ and relative humidity is 50 +/- 5%.
Equipped with 13 shaft diaMeters from 2 to 32mm, it can accurately determine the cracking performance of coatings; support 1.0mm thickness sample testing, manual operation to ensure smooth and controllable bending process, meeting standard laboratory Environmental requirements.
Measurement width 200mm, thickness within 1.5mm test plate, stainless steel cone diaMeter range 3.2-38 mm, anodic oxidation aluminum material, complete 180 ° bending test within 15 seconds.
Equipped with 2 to 12mm eight diaMeter stainless steel cylindrical mandrel, in the form of hinged bending, in line with GB6742 standard, suitable for Coating bending performance testing.
Equipped with a total of 12 shaft Rods of 2-32mm, it can test the 1.0mm thickness sample, and test the anti-cracking performance of the coating through 180 ° bending, which is easy to operate and accurate.
Equipped with 13 kinds of diaMeter shaft Rods, covering the range of 2-32mm, can detect 1.0mm thickness samples, evaluate the film anti-cracking performance through different bending radii, easy and accurate operation.