Adopt the circular roller scratch method to evaluate the adhesion grade, describe the adjustable diaMeter of 0-10.5 mm, equipped with four weights to achieve 200-1000g loading, table Travel ≥ 80mm, manual operation is stable and reliable.
The adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel ≥ 80mm. The integrity of the paint film was evaluated by seven grades, and the operation was simple and conformed to the GB/T1720 standard.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0-10.5 mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
The fully automatic electronically controlled hydraulic pump provides smooth and continuous pulling force with +/- 1% accuracy, built-in rechargeable battery supports 200 tests, and IP65 Protection Rating ensures durability.
Using digital touch screen control, the test speed is adjustable from 0-40mm/s, the load range is 0-4000g, the minimum increment is 50g, and it is equipped with a variety of weights and special scribing needles to accurately determine the film scratch resistance performance.
Control system using servo motor, scratch speed 254mm/min, weight free lifting, ensure that the needle parts accurately fall on the workpiece, to achieve automatic scratch and zero operation.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Using electric Dial design, the scratch length can reach 60mm, the load range is 0-2000g, and the physical characteristics of the coating are characterized by the anti-penetration ability of the scribing needle.
Rotation speed 80rpm, Working Travel 80mm, in line with international standards, to ensure accurate and reliable film adhesion assessment.
The scribing needle is used to act vertically on the film, the load range is adjustable from 0-2000g, the minimum increment is 50g, and the diaMeter of the steel ball is 1mm, which can accurately determine the minimum weight required to cut the paint film.
Hand crank type is easy to operate, load 1000g +/- 1g, scratch speed about 1mm/s, test angle 45 °, standard 6B-6H pencil, in line with a number of international standards, through the pencil Hardness grade to accurately evaluate the scratch performance of the paint film.
The circular stainless steel liner is used to prevent condensation and dripping, the copper tube bell mouth is designed with good air tightness and low water consumption, and the special high temperature foaming material improves the pressure life. It is equipped with a 16L large-capacity water Tank and an automatic water replenishment system.
Using 0.5mm tungsten carbide tip, the spherical test point can scratch 2000 90mm long scratches without damage after durability test, the design is comfortable and stable, and it is suitable for regular interval scratch operation in corrosion test.
Using positive pressure test principle, Measurement range 0~ 1.6MPa, fully automatic operation, support three test modes, built-in calibrating program, suitable for quantitative measurement of various sealing performance indicators.
The circular cutter is designed with eight incisions and 1mm spacing between the teeth. It is suitable for strong substrate adhesion testing with a Coating thickness of less than 60 microns and meets the requirements of ISO 2409.