Using pure mechanical design, the coating performance is measured by conical mandrel bending test plate, the test plate size is 100mm × 180mm, the thickness is less than or equal to 0.8mm, and the operation is simple and reliable.
Using conical mandrel design, can measure the cracking resistance and elongation of the coating, the thickness of the test plate supports 0.8mm, easy to operate without power supply, to meet a variety of standard test requirements.
The conical mandrel bending range is 3.1 to 38mm, and the plate thickness can be tested by 0.8mm. The panel is instantly locked and unlocked with a fast lever handle, which is convenient for operation.
The tapered shaft size range is 3.2~ 38mm, and the shaft length is 203mm, which can test the cracking and disbonding performance of the paint film under bending conditions, in line with international standards.
Measurement width 200mm, thickness within 1.5mm test plate, stainless steel cone diaMeter range 3.2-38 mm, anodic oxidation aluminum material, complete 180 ° bending test within 15 seconds.
With a conical mandrel design, the resilience of the coating can be evaluated in a single test in the diaMeter range of 3.1 to 38mm, and the thickness of the test plate is less than or equal to 0.8mm.
The test bending angle is less than 45 degrees, suitable for steel plate thickness 0.5~ 1.0mm and Aluminum Panel thickness 0.5~ 2.0mm. The gear pair and crank lifting mechanism are used to achieve T-shaped bending, which is easy to operate.
A bending angle is less than 45 degrees, can test 0.5~ 1.0mm Film thickness sample, flattening mechanism stroke is not less than 10mm, using crank lifting mechanism to achieve T-shaped bending test.
The gear pair and crank lifting mechanism are used to achieve accurate bending, the first bending angle is less than 45 °, the flattening mechanism Travel ≥ 10mm, which can test 0.5-2 mm thickness plates and support OT to T bend test.
The cone shaft is used to test the anti-cracking performance of coatings with different curvatures. The size of the cone shaft is Φ 3.1~ 38mm, the volume is small and the weight is light, which is convenient for laboratory and field use.
With a bending angle of 135 degrees and a folding speed of 175 times per minute, it can apply a test load of 4.91N to 14.72N, and the automatic counting function accurately records the number of breaks, which is suitable for material durability testing.
Equipped with 2 to 12mm eight diaMeter stainless steel cylindrical mandrel, in the form of hinged bending, in line with GB6742 standard, suitable for Coating bending performance testing.
Conical mandrel size is 3.1~ 38 mm, length 203 mm, stainless steel material, wear resistance and corrosion resistance, can test the bending performance of steel, aluminum alloy and plastic sample, easy to operate.
The cone shaft length is 203mm and the large end diaMeter is 38mm, which can test the cone bending resistance of a single layer or the entire coating system separately. Operating temperature is 23 +/- 2 ℃ and relative humidity is 50 +/- 5%.
The instrument is equipped with eight kinds of diaMeter stainless steel cylindrical mandrel, which adopts the form of hinge connection bending, which can accurately test the bending deformation of coatings under different diaMeters to ensure the test Reliability.