The instrument uses 241 +/- 6mm tire uniform rolling detection, wet film thickness 200um +/- 20um, every 30 seconds, repeability test, accurate determination of non-stick tire drying time, suitable for marking Coating quality control.
The kit can realize automatic grinding fineness Gauge operation, improve test Repeatability, suitable for standard scraper fineness Meter supporting use, simplify the experimental process.
A wet film with a film thickness of 50~ 675 μ m was prepared by using a coating scraper, and the sag property was observed when placed vertically. The maximum thickness without sag was expressed, which was suitable for Paints testing.
The tire size of the instrument is Φ 241 +/- 6mm, weight 15.8 +/- 0.2kg, dedicated to marking Coating drying time test, easy to operate, accurate and reliable results.
Adopt high-quality alloy steel scraper, Hardness and wear resistance and corrosion resistance; Magnetic suction design for quick replacement and cleaning; Film Film thickness 0~ 4500 μ m free adjustment, resolution up to 10 μ m, error only +/- 2 μ m.
Using removable scraper and vacuum adsorption system, Spreader accuracy +/- 0.003mm, Spreader rate 5~ 180mm/s, heating temperature up to 180 ℃, improve film Stability and uniformity.
Adopt removable scraper for easy cleaning and replacement, with bracket design to improve running Stability; Spreader accuracy of +/- 0.003mm, Film thickness range of 0~ 10mm adjustable, effective Spreader area of 400 * 300mm, through stepless speed control to ensure uniform Spreader.
High-quality alloy steel scraper, Hardness and wear resistance and corrosion resistance, Film thickness adjustment range 0-4500 μ m, magnetic suction design for quick replacement and cleaning, differential head accuracy of +/- 2 μ m to ensure uniform and stable film.
Spreader width 250mm, wet film thickness adjustment range 0-4500μm, scraper error +/- 2μm, High Accuracy Differential Head Control to meet the needs of various materials Moulding.
High-quality alloy steel scraper accuracy of +/- 2μm, magnetic suction design for easy cleaning and replacement, Film thickness adjustment range of 0-4500μm to meet the needs of different materials Moulding, acid and alkali corrosion bracket to ensure long-term stable use.
Effective Spreader width 300mm, suitable for all kinds of scraper type Film Applicators, to ensure the uniformity of Spreader, improve the film accuracy and conformity in the experiment or pRoduction.
Adopting Japanese I15 standard design, the external aperture is 6.0 +/- 0.5mm, and the internal aperture is 3.5 +/- 0.05mm, which can quickly measure Coating viscosity and take the average value of three measurements to ensure accuracy.
The instrument is designed with a heavy hammer structure, with a weight mass of 6600g +/- 33g, which is suitable for the bending performance test of reflective film. It is simple to operate and safe and reliable to measure, and meets the requirements of national standards.
Equipped with 0.5/0 7/1.0 mm three thickness die frame, using baseplate fixed structure to ensure film uniformity, metal drawdown blade design to meet long-term use needs.
The scraping speed is adjustable from 10-100mm/s, and the drawdown blade load 1.75-6 kg is adjustable. It is used with High Accuracy GrindoMeter to avoid personnel operation errors and improve test conformity.