The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0-10.5 mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Maximum load 50Kg, Test speed 10~ 60mm/min adjustable, using pointer sensing mode, effective Travel 0~ 360mm, suitable for vertical angle disbonding test.
Rotation speed 80rpm, Working Travel 80mm, in line with international standards, to ensure accurate and reliable film adhesion assessment.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
The adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel ≥ 80mm. The integrity of the paint film was evaluated by seven grades, and the operation was simple and conformed to the GB/T1720 standard.
Tack is good and non-degumming, adhesion reaches 7.6 N/cm, mass performance is stable, suitable for cross-cut adhesion testing, to ensure accurate film integrity assessment.
35Mm cross-cut length and 1mm pitch design, stainless steel material to ensure dimensional accuracy, equipped with tape and brush for film adhesion testing.
Equipped with three swirl/spin cutter heads, the tooth spacing is 1mm, 2mm and 3mm respectively, and it is designed according to ISO2409 standard for accurate evaluation of coating adhesion performance.
Adopt the circular roller scratch method to evaluate the adhesion grade, describe the adjustable diaMeter of 0-10.5 mm, equipped with four weights to achieve 200-1000g loading, table Travel ≥ 80mm, manual operation is stable and reliable.
Adopting a stepper motor automatic positioning and electromagnetic release system, the swing period is 1.4 seconds, and the steel ball diaMeter is 5 mm, providing visual and acoustic test end signals.
Set cross-cut adhesion, film thickness and Buchholz Crowd Hardness three test functions in one, cross-cut knife 6 blade spacing 1mm/2mm, Crowd knife load 500 +/- 5g, using the destruction Measurement principle.
Vacuum hardened stainless steel material, cutting depth can be accurately adjusted, weight only 352g easy to carry, suitable for different film thickness and substrate adhesion testing.
Steel hammer mass 800 +/- 3g, drop 0.2~ 0.3m, stable measurement of reflective film disbonding degree, suitable for standard test conditions placed 24h samples to ensure safe and reliable measurement.
It adopts 11-tooth cutter design, provides four spacing options from 1mm to 3mm, and is suitable for paint film adhesion testing with a thickness of less than 250mm. The operation is simple and the results are accurate and reliable.
The hand wheel drive is used to realize the synchronization of the table movement and the needle drawing circle, the drawing diaMeter can be adjusted from 0 to 10.5mm, and it is equipped with 808 stylus and graded weight.