Hydraulic pump is used to uniformly pull off the test column, the speed does not exceed 1MPa/s, the test force is directly displayed by liquid crystal, and the adhesion failure and cohesion failure can be distinguished, with an accuracy of +/- 1% F.S.
Accessories can detect buttons and other fixed strength, to prevent loosening caused by sharp edge angle damage, the maximum tensile force of 30kg, suitable for clothing toys footwear and other pRoducts adhesion testing.
Mechatronics design integrated measurement display circuit, manual operation with 20mm/50mm kit, range of 10KN accuracy ≤ +/- 1% F. S, with linear correction and automatic clearing function for a variety of coating platings strength test.
Maximum load 50Kg, Test speed 10~ 60mm/min adjustable, using pointer sensing mode, effective Travel 0~ 360mm, suitable for vertical angle disbonding test.
Tack is good and non-degumming, adhesion reaches 7.6 N/cm, mass performance is stable, suitable for cross-cut adhesion testing, to ensure accurate film integrity assessment.
Set cross-cut adhesion, film thickness and Buchholz Crowd Hardness three test functions in one, cross-cut knife 6 blade spacing 1mm/2mm, Crowd knife load 500 +/- 5g, using the destruction Measurement principle.
The scribing needle is used to act vertically on the film, the load range is adjustable from 0-2000g, the minimum increment is 50g, and the diaMeter of the steel ball is 1mm, which can accurately determine the minimum weight required to cut the paint film.
The adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel ≥ 80mm. The integrity of the paint film was evaluated by seven grades, and the operation was simple and conformed to the GB/T1720 standard.
Made of stainless steel, the cutter tooth spacing is 1-3mm, the cut mark length is 35mm, and the coating is cut through the grid pattern, and the adhesion effect is evaluated according to the six-level classification, which is suitable for a variety of surface tests.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0-10.5 mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Hydraulic system measurement coating adhesion, accuracy control within +/- 1% full scale, optional 10mm to 50mm more than the kit size, self-positioning characteristics to ensure smooth rough surface measurement results accurate and reliable.
Rotation speed 80rpm, Working Travel 80mm, in line with international standards, to ensure accurate and reliable film adhesion assessment.
Hydraulic system measurement coating adhesion, accuracy control within +/- 1%, equipped with self-positioning kit to ensure smooth and rough surface measurement results consistent, optional 10mm to 50mm variety of kit specifications.
Equipped with three swirl/spin cutter heads, the tooth spacing is 1mm, 2mm and 3mm respectively, and it is designed according to ISO2409 standard for accurate evaluation of coating adhesion performance.
Hydraulic system measurement coating adhesion, accuracy control within +/- 1% full scale, equipped with multi-function digital display, can automatically calculate different kit size results, self-positioning kit to adapt to various surfaces.