Using conical mandrel design, can measure the cracking resistance and elongation of the coating, the thickness of the test plate supports 0.8mm, easy to operate without power supply, to meet a variety of standard test requirements.
The conical mandrel bending range is 3.1 to 38mm, and the plate thickness can be tested by 0.8mm. The panel is instantly locked and unlocked with a fast lever handle, which is convenient for operation.
Using pure mechanical design, the coating performance is measured by conical mandrel bending test plate, the test plate size is 100mm × 180mm, the thickness is less than or equal to 0.8mm, and the operation is simple and reliable.
The thickness of the pressurable steel plate Aluminum Panel is 0.2~ 1.5mm, the weight of the whole machine is 50kg, and the compact shape is only 300 * 300 * 190mm, which meets the NCCA standard T-Bend test method.
With a conical mandrel design, the resilience of the coating can be evaluated in a single test in the diaMeter range of 3.1 to 38mm, and the thickness of the test plate is less than or equal to 0.8mm.
Equipped with 2 to 12mm eight diaMeter stainless steel cylindrical mandrel, in the form of hinged bending, in line with GB6742 standard, suitable for Coating bending performance testing.
With +/- 0.1% accuracy Sensor and 0.01mN resolution, it supports 1-92 ° bending angle adjustment and 0.5-50 °/sec angular speed control, with self-Adjustment and three independently adjustable test angles, suitable for 0.01-5 thickness materials.
Support 0.1-1 steel plate and 0.1-2 Aluminum Panel test, can complete 0T to 1T multi-stage bending, equipped with pliers pressing device and tape adhesion inspection function, to meet the standard bending test process.
Conical mandrel size is 3.1~ 38 mm, length 203 mm, stainless steel material, wear resistance and corrosion resistance, can test the bending performance of steel, aluminum alloy and plastic sample, easy to operate.
It can test the cracking of the paint film after bending 180 degrees in 1-3 seconds, and the diaMeter range of the shaft Rod is 2-32mm. It is suitable for the test plate with a thickness of not more than 1.0mm. Quick evaluation of flexibility.
Equipped with 13 kinds of diaMeter shaft Rods, covering the range of 2-32mm, can detect 1.0mm thickness samples, evaluate the film anti-cracking performance through different bending radii, easy and accurate operation.
The cone shaft is used to test the anti-cracking performance of coatings with different curvatures. The size of the cone shaft is Φ 3.1~ 38mm, the volume is small and the weight is light, which is convenient for laboratory and field use.
Equipped with 8 kinds of diaMeter shaft Rods from 2 to 12mm, the 180 degree bending test can be completed in 1-3 seconds, and the anti-cracking performance of the paint film can be evaluated with the smallest shaft Rod diaMeter, which is easy to operate.
Measurement width 200mm, thickness within 1.5mm test plate, stainless steel cone diaMeter range 3.2-38 mm, anodic oxidation aluminum material, complete 180 ° bending test within 15 seconds.
The tapered shaft size range is 3.2~ 38mm, and the shaft length is 203mm, which can test the cracking and disbonding performance of the paint film under bending conditions, in line with international standards.