The equipment evaluates the performance by recording the number of wipes required for coating damage, the Wipe Test Frequency is 20~ 60cpm, the friction load is 1000 +/- 10g, and the standard test method is supported.
Travel 100mm, Frequency 100cpm, friction load 1000 +/- 100g, grinding head area 2cm ², can accurately test the coating solvent performance.
The equipment adopts 1000 +/- 10g friction load and 0~ 60cpm wiping frequency, and the number of times required for coating damage is determined by reciprocating wiping, and the automatic counting function ensures the accuracy of the test.
The wiping stroke is 120mm, the wiping frequency is 100cpm, and the friction load is 1000g. The number and speed of wiping can be set, and the automatic stop function ensures the accuracy of the test.
Employing an extrusion production process, the coating thickness is 105 microns, the coating width reaches 300 mm, and the coating accuracy can achieve 0.5 microns, ensuring coating uniformity and high-precision control.
Using the formed pRoduction process, Coating Weight is about twice that of the wire-wound coating Rod, wet film thickness is 13μm, film accuracy reaches 0.5 μm, and the material is 304 stainless steel.
Spreader 13 micron wet film thickness, application width up to 300mm, 304 stainless steel for durability and precise coating control.
Adjustable application width, with automatic Spreader function, easy to operate, Repeatability is good, suitable for a variety of samples of laboratory prepative.
The extrusion production process ensures uniform coating, with a wet film thickness of 60μm meeting the demands of precise experiments. The 304 stainless steel material is durable and easy to clean, making it suitable for diverse coating performance tests.
Using the formed pRoduction process, the wet film thickness is 6 microns, the accuracy is 0.5 microns, the cleaning is convenient and there is no worry of broken wire, to ensure the precision and durability of the coating prepative.
Wound wire design, wet film thickness 125.7 microns, coating width 300 mm, stainless steel material ensures durability and precise coating effect.
Using a wire-wound coating process, with a wet film thickness of 32.0 μm and a coating width of 300 mm, it is suitable for substrates prone to curling and convexity, enabling uniform wet film coating, with a wire diaMeter of 0.36 mm.
Wet film thickness 29.7 microMeters, coating width 300 milliMeters, using stainless steel wire-winding process, suitable for experimental sample preparation.
The punch is pushed to the test plate at a constant speed of 0.2 +/-0.1mm/s, and the thickness range of the test plate is 0.30-1. 25mm, which can detect the degree of coating cracking and is suitable for testing of various materials.
Formed design Coating Weight is about twice the wide-wound drawdown bar, wet film thickness 13μm, film accuracy of 0.5 micron, 304 stainless steel material to ensure durability.