    Wet film comb wet film thickness Gauge

    Overview Products Knowledge Terms
    The wet film comb measures coating thickness using its tooth-like structure. The comb is pressed vertically into the wet film, and the thickness is determined by observing the teeth that become wet, with the corresponding scale indicating the measurement. It is used for rapid monitoring of coating and ink application quantities during construction to ensure coating uniformity.
    Selection
    When selecting, consider that the measurement range should cover common coating thicknesses, the stainless steel material should be corrosion-resistant, and the scale should be clear and easy to read. Choose the appropriate tooth shape based on the coating characteristics: use a standard comb for flat substrates and a curved comb for curved substrates. Verify the measurement certification to ensure data reliability.
    type
    Maximum range
    Minimum scale
    precision
    material
    shape

    Terms

    Color development wheel
    Wet Film Thickness Gauge
    Micrometer Coater
    Wet Film Applicator
    Wet film wheel gauge
    Planar Coating Machine
    Film Applicator
    Micron-adjustable film applicator
    Doctor Blade Film Coater
    Gap-type paint film applicator

    Instruments

    YONGLIDA SHG-200 wet film thickness Gauge Wet Film Comb stainless steel 20~ 200μm range
    YONGLIDA SHG-200 wet film thickness Gauge Wet Film Comb stainless steel 20~ 200μm range

    Made of stainless steel, the thickness is only 1.5mm, the range is 20~ 200μm, Division 20μm, the card design is convenient for quick measurement of wet-film Coating thickness on site.

    $ 119.00
    PUSHEN SHG 50-950 Comb type wet film thickness Gauge, stainless steel one-sided type range to 950μm
    PUSHEN SHG 50-950 Comb type wet film thickness Gauge, stainless steel one-sided type range to 950μm

    Made of precision stainless steel, with a range of 50 to 950 μm, the 10-step tooth design can accurately measure wet film thickness, ensure painting mass and avoid material waste.

    $ 109.00
    PUSHEN SHG 10-100 comb type wet film thickness Gauge, stainless steel unilateral type 10~ 100μm range
    PUSHEN SHG 10-100 comb type wet film thickness Gauge, stainless steel unilateral type 10~ 100μm range

    The stainless steel material is durable, the range is 10~ 100μm Division 10μm, the unilateral design is convenient for vertical pressing into the wet-film measurement, and the number of teeth 10 can accurately read the thickness value between the infiltrated and uninfiltrated teeth.

    $ 109.00
    DUBAN DB10-2000 Wet Film Comb polygon wet film thickness measurement instrument
    DUBAN DB10-2000 Wet Film Comb polygon wet film thickness measurement instrument

    Polygonal structure design, range 25~ 2032µm, in line with GB/T1764-79, GB/T134522-92, ISO 2808-74 standards, suitable for Paints, varnish and other Coating wet film thickness measurement.

    $ 106.00
    YONGLIDA SHG-750 wet film thickness Gauge Wet Film Comb Stainless Steel 50-950 microns
    YONGLIDA SHG-750 wet film thickness Gauge Wet Film Comb Stainless Steel 50-950 microns

    Stainless steel material is sturdy and durable, with a range of 50-950 microns, Division 50 and 100 microns, and a compact shape of only 65 * 43 * 1.5mm, suitable for rapid measurement of wet film thickness on site.

    $ 119.00
    YONGLIDA SHG-100 wet film thickness Gauge Wet Film Comb 10~ 100μm range
    YONGLIDA SHG-100 wet film thickness Gauge Wet Film Comb 10~ 100μm range

    Made of stainless steel, the range is 10~ 100μm, Division 10μm, Dimension 65 * 36 * 1.5mm, suitable for Paints, varnish and other Coating Coating thickness measurement.

    $ 119.00
    PUSHEN SHG 20-200 Comb type wet film thickness Gauge, stainless steel unilateral type 20~ 200μm
    PUSHEN SHG 20-200 Comb type wet film thickness Gauge, stainless steel unilateral type 20~ 200μm

    Made of stainless steel, durable and repeatability; range 20~ 200μm, Division 20μm, step number of teeth 10, unilateral design is convenient for vertical pressing into wet-film measurement, in line with international standards.

    $ 109.00
    JINGKELIAN QUL (0-150) wet film thickness Gauge
    JINGKELIAN QUL (0-150) wet film thickness Gauge

    In line with ISO2808-1974 standard, the range is 0~ 150μm, the accuracy is not more than 5μm, can measure the wet film thickness and estimate dry-film thickness, suitable for laboratory and pRoduction control.

    $ 127.00
    YONGLIDA SHG-700 wet film thickness Gauge Wet Film Comb Stainless Steel 250~ 700 microns
    YONGLIDA SHG-700 wet film thickness Gauge Wet Film Comb Stainless Steel 250~ 700 microns

    Range 250~ 700 microns, Division 45 microns, made of stainless steel, Dimension 65 * 43 * 1.5 mm, suitable for on-site construction environment.

    $ 119.00
    JINGKELIAN QUL (0-500) wet film thickness Gauge 0~ 500μm range
    JINGKELIAN QUL (0-500) wet film thickness Gauge 0~ 500μm range

    In line with ISO2808 standard, the range is 0~ 500μm, the accuracy is not more than 5μm, can measure the wet film thickness and estimate dry-film thickness, suitable for laboratory and pRoduction site.

    $ 127.00
    YONGLIDA QUL-500 wet film thickness Gauge Thickness Wheel Stainless steel roller type 0~ 500μm
    YONGLIDA QUL-500 wet film thickness Gauge Thickness Wheel Stainless steel roller type 0~ 500μm

    Roller type design, range 0~ 500μm, stainless steel material to ensure durability, suitable for on-site rapid measurement wet film thickness, in line with a number of execution standards.

    $ 146.00
    PUSHEN SHG 250-700 Comb type wet film thickness Gauge, stainless steel unilateral type Range 250-700μm
    PUSHEN SHG 250-700 Comb type wet film thickness Gauge, stainless steel unilateral type Range 250-700μm

    Made of precision stainless steel, durable and repeatability; range 250-700 μm, Division 50 μm; in line with international measurement standards to ensure accurate painting thickness control.

    $ 109.00
    RDS 52 #3/8 Applicator Rod wire-wound stainless steel coating coating bar wet film thickness 118.9μm
    RDS 52 #3/8 Applicator Rod wire-wound stainless steel coating coating bar wet film thickness 118.9μm

    Wire-wound design, wet film thickness 118.9μm, diaMeter 9.5mm, stainless steel material, wear resistance and corrosion resistance, suitable for preparing specific film thickness wet-film.

    $ 167.00
    OSP-10/250 coating Rod 10 micron wet film thickness
    OSP-10/250 coating Rod 10 micron wet film thickness

    Spreader 10 micron wet film thickness, 304 stainless steel material, easy to clean unbroken wire, provide customized services.

    $ 157.00
    TRUIT TR 5501/700 Single-sided wet-film thickness Gauge 250~ 700μm
    TRUIT TR 5501/700 Single-sided wet-film thickness Gauge 250~ 700μm

    Made of corrosion-resistant stainless steel, the thickness range is 250~ 700 μm, Graduation 50 μm, and fast and accurate wet film thickness measurement is achieved through the toothed structure.

    $ 102.00

    Articles

    Laboratory rod coater for submicron wet film preparation of photoresist.
    This article introduces the process of using a laboratory bar coater to prepare submicron wet films of photoresist.
    Application of Wet Film Wheel Gauge in Continuous Measurement of Wet Film Thickness for Large-Area Coatings
    The wet film wheel gauge is a mechanical tool used to measure the thickness of wet coatings, operating based on the geometric relationship of three coaxial disks (two parallel outer wheels on the sides and an eccentric inner wheel in the middle).
    Operating specifications for on-site measurement of coating wet film thickness using wet film combs
    This article introduces the operational standards for on-site measurement of coating wet film thickness using a wet film comb gauge. First, it explains the measurement principle of the wet film comb gauge, which involves estimating the thickness by observing the extent to which the teeth of the gauge are coated with the paint.
    Selection of wet film thickness gauge range and accuracy requirements for comb teeth spacing.
    When selecting a wet film thickness gauges, the key considerations are the measurement range and the accuracy of the comb teeth spacing. The range should cover the coating thickness with a slight margin to avoid being too small for measurement or too large, which could reduce resolution.
    Wet film thickness gauge measures the wet film thickness of varnish.
    The wet film thickness gauge is a mechanical tool used to measure the thickness of liquid varnish coatings. It operates by rolling the gauge so that the tips of its teeth contact the substrate and leave marks. The thickness value is then obtained by the operator reading the scale of the first tooth that becomes coated with the varnish.
    Wet film applicator for applying color paint to a specified wet film thickness.
    A wet film applicator is a laboratory tool used to apply a predetermined thickness of wet paint film onto a flat substrate, providing the foundation for subsequent dry film performance testing.
    Operating Specifications and Result Interpretation of Paint Fineness Gauges
    The fineness gauge is used to measure the dispersion of particles in paint. During operation, the sample should be applied to the groove under standard conditions, and a scraper is used to spread it evenly to form a wet film. The particle visibility is then observed under appropriate lighting, and the fineness value is read from the corresponding scale.
    Application of Two-Step Method with Pre-Coating and Fine-Coating in Eliminating Bubble Defects for Dual-Blade Coater
    The dual-blade coater employs a two-step method of pre-coating and precision coating to eliminate bubble defects during the coating process. In the pre-coating stage, high shear force is applied to break the bubbles in the slurry, causing them to rupture and rise to the surface. The precision coating stage then precisely controls the coating thickness, removing any remaining bubbles to form a uniform wet film.
    Key Points for Controlling Coating Longitudinal Uniformity with Manual Rod Coater Constant Speed Dragging Techniques
    This article discusses how to control the longitudinal uniformity of the coating by dragging at a constant speed when using a manual wire rod coater. A constant-speed drag is crucial, as it directly determines the consistency of the wet film thickness.
    Key Points for Wet Film Thickness Control in the Preparation of Fluorocarbon Coatings for Photovoltaic Backsheets Using Automatic Film Coating Machines
    This article introduces the key points of controlling wet film thickness in the preparation of fluorocarbon coatings for photovoltaic backsheets using an automatic coating machine. Wet film thickness directly affects the performance and uniformity of the coating after curing, making its control crucial.
    Derivation and Validation of the Quantitative Relationship between Wire Diameter and Wet Film Thickness in Wire Wound Coating Bars
    This paper investigates the relationship between the wire diameter in a wire-wound rod coater and the wet film thickness. Theoretically, under ideal conditions, the wet film thickness is approximately half of the wire diameter.
    Paper Thickness Gauge for Determining Paper Thickness and Apparent Density
    This article explains how to measure paper thickness and apparent density using a paper thickness gauge. Thickness refers to the vertical distance between the two sides of paper under standard pressure, while apparent density is calculated by dividing the basis weight by the thickness, reflecting the compactness of the paper.
    The correct method for using a wet film thickness gauge.
    The wet film thickness gauge is used to measure the thickness of uncured coatings. It determines the value by reading the scale through contact with the wet film using a toothed structure, which is crucial for controlling dry film thickness and estimating material usage.
    Control of Wet Film Thickness—Field Operation Comparison Between Wheel Gauge and Comb Gauge
    This article compares two tools for measuring wet film thickness: the wheel gauge and the comb gauge. When selecting a tool, factors such as coating characteristics, application environment, and precision requirements must be considered. Additionally, proper operation and environmental influences should be taken into account to ensure coating quality.
    Rapid Assessment of Paint Hiding Efficiency by Minimum Wet Film Thickness Method
    This article introduces a method for rapidly evaluating the hiding efficiency of coatings—the minimum wet film thickness method. Traditional methods are time-consuming, whereas this approach quantifies hiding power by measuring the minimum wet film thickness required for the coating to completely hide the substrate, making it simple and quick to operate.