Using photothermal method to achieve non-destructive measurement, Measurement range 0-300μm, accuracy +/- 3%, can be measured in any shape of the sample including the frame and edge.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0-10.5 mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Using mechanical measurement method, Measurement range 0~ 1mm, accuracy ≤ 0.005mm, Graduation 0.001mm, probe diaMeter Φ 5mm, suitable for flat film and sheet, providing two probe pressure options.
Adopt magnetic thickness measurement method, measurement range 0-1250μm, error +/- 3%, with continuous and single measurement mode, can store 1560 measurement data, support a variety of calibrating methods.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Using mechanical measurement method, Measurement range 0~ 1mm, accuracy ≤ 0.005mm, Graduation 0.001mm, providing two probe pressure options to adapt to different testing needs.
The device adopts destructive measurement, resolution +/- 0.001mm, can carry out V-shaped incision, grid cutting and Cedar test, directly observe Coating thickness and Cedar length, support multi-layer film analysis.
Measuring wet-film flow thickening in the vertical state, controlling the physical performance of the coating to select the appropriate wet film thickness to ensure uniform film thickness, Film thickness range 450-675μm, in line with GB/T 9264 and ASTM D 3730 standards.
Adopt drawdown Bar & blade double coating method, coating speed 1-300mm/s stepless speed regulation, film thickness control accuracy of +/- 0.001mm, clamshell Drawdown blade head design is easy to clean operation.
In line with ISO2808-1974 standard, the range is 0~ 150μm, the accuracy is not more than 5μm, can measure the wet film thickness and estimate dry-film thickness, suitable for laboratory and pRoduction control.
The formed pRoduction process is adopted, the wet film thickness is 42 μm, the application width is 60mm, the preparatory coating is uniform and the film thickness is accurately controllable, which is convenient for comparative analysis by conversion of dry-film thickness by Solid content.
Using smooth steel bar design, no winding steel wire or pressurized groove, film thickness is 0μm, diaMeter 6.35mm, total length 400mm, suitable for machine control film thickness.
The 4-sided design can complete different thickness films at one time, using wear-resistant and corrosion-resistant stainless steel material, film thickness 150-300μm, application width 105mm, can accurately control wet-film or dry-film thickness.
In line with ISO2808 standard, the range is 0~ 500μm, the accuracy is not more than 5μm, can measure the wet film thickness and estimate dry-film thickness, suitable for laboratory and pRoduction site.
304 stainless steel material, wet film thickness of 200 μ m, Spreader width of 250mm, formed pRoduction process to ensure uniform film, suitable for precision experimental needs.