Using photo paper smooth surface combination technology, observing the imprint after applying a uniform load, the pressure range of the probe is 50-250N, and the diaMeter of the rubber probe is Φ 40mm, which can accurately evaluate the chalking grade of the paint film.
Wire-wound design, film thickness 120 microns, total length 37.5cm, effective application width 25.5cm, stainless steel material to ensure durability and uniform Spreader.
The pressure range of the probe is 50~ 250N, the diaMeter of the rubber probe is 40mm, and the degree of paint film chalking is evaluated by comparing the imprint of the photo paper with the standard sample, which is suitable for the detection of various environmental factors.
A wet film with a film thickness of 50~ 675 μ m was prepared by using a coating scraper, and the sag property was observed when placed vertically. The maximum thickness without sag was expressed, which was suitable for Paints testing.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Adopt high-quality alloy steel scraper, Hardness and wear resistance and corrosion resistance; Magnetic suction design for quick replacement and cleaning; Film Film thickness 0~ 4500 μ m free adjustment, resolution up to 10 μ m, error only +/- 2 μ m.
High-quality alloy steel scraper, Hardness and wear resistance and corrosion resistance, Film thickness adjustment range 0-4500 μ m, magnetic suction design for quick replacement and cleaning, differential head accuracy of +/- 2 μ m to ensure uniform and stable film.
Using removable scraper and vacuum adsorption system, Spreader accuracy +/- 0.003mm, Spreader rate 5~ 180mm/s, heating temperature up to 180 ℃, improve film Stability and uniformity.
The drying process of paint film and putty film can be accurately measured by using circular track needle design, equipped with four different radius needle (R0.25/0.5/1.0/1 mm), and the track period is 24h/r.
Adopt removable scraper for easy cleaning and replacement, with bracket design to improve running Stability; Spreader accuracy of +/- 0.003mm, Film thickness range of 0~ 10mm adjustable, effective Spreader area of 400 * 300mm, through stepless speed control to ensure uniform Spreader.
Spreader width 250mm, wet film thickness adjustment range 0-4500μm, scraper error +/- 2μm, High Accuracy Differential Head Control to meet the needs of various materials Moulding.
High-quality alloy steel scraper accuracy of +/- 2μm, magnetic suction design for easy cleaning and replacement, Film thickness adjustment range of 0-4500μm to meet the needs of different materials Moulding, acid and alkali corrosion bracket to ensure long-term stable use.
Using 200g weight and 1cm ² bottom area design, in line with GB/T 1728 standard, through the filter paper test method to accurately determine the film surface drying and practical drying time, easy to operate, reliable results.
Using 500g weight and 1cm ² bottom area, after tacking the paint film at a specific temperature Humidity test, the operation is simple, and the drying state is evaluated by the adhesion of the filter paper fibers.
The kit can realize automatic grinding fineness Gauge operation, improve test Repeatability, suitable for standard scraper fineness Meter supporting use, simplify the experimental process.