The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0-10.5 mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Electric Circle-drawing is used to ensure uniform speed and constant strength, Travel 20-80mm adjustable, Rotation speed 10-120 +/- 1 rpm adjustable, equipped with automatic judgment prompts and precision dual rail system to improve test Repeatability and data accuracy.
Rotation speed 80rpm, Working Travel 80mm, in line with international standards, to ensure accurate and reliable film adhesion assessment.
The adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel ≥ 80mm. The integrity of the paint film was evaluated by seven grades, and the operation was simple and conformed to the GB/T1720 standard.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Adopt the circular roller scratch method to evaluate the adhesion grade, describe the adjustable diaMeter of 0-10.5 mm, equipped with four weights to achieve 200-1000g loading, table Travel ≥ 80mm, manual operation is stable and reliable.
Double pointer design for easy reading, Pin Travel 0~ 2.5mm, Measurement range 0~ 100HD, error +/- 1HD, lightweight and portable only 0.16kg, suitable for on-site Hardness detection.
With tracking pointer and peak pointer double pointer design, pressing needle Travel 0-2.5 mm, Measurement range 10-90Hc, suitable for material testing with pressure above 0.049MPa when the compression rate is 50%, and can be matched with test bracket to improve Stability.
The hand wheel drive is used to realize the synchronization of the table movement and the needle drawing circle, the drawing diaMeter can be adjusted from 0 to 10.5mm, and it is equipped with 808 stylus and graded weight.
Adopting the principle of the inclined rolling ball method, the adhesion is measured by the short contact between the steel ball and the sample, the adjustment range of the tilt angle is 0-60 °, and the rolling ball of 1/32 to 1 inch is supported. The width of the test area is 80mm.
Tack is good and non-degumming, adhesion reaches 7.6 N/cm, mass performance is stable, suitable for cross-cut adhesion testing, to ensure accurate film integrity assessment.
The adhesive force of the tape is 4.3N/cm, and the principle of cross-cut method is adopted, which is suitable for adhesion testing. The performance is stable and non-degumming, and the test results are accurate and reliable.
Vacuum hardened stainless steel material, cutting depth can be accurately adjusted, weight only 352g easy to carry, suitable for different film thickness and substrate adhesion testing.
Made of stainless steel, the cutter tooth spacing is 1-3mm, the cut mark length is 35mm, and the coating is cut through the grid pattern, and the adhesion effect is evaluated according to the six-level classification, which is suitable for a variety of surface tests.
Pin Travel 0~ 2.5mm, Measurement range 0~ 100HA, Error +/- 1HA, Dual pointer design can display real-time and peak Hardness value at the same time, easy to use handheld or rack.