The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
It can measure the ability of the paint film to deform with the substrate without damage. It is equipped with a shaft Rod with a diaMeter of 50mm and 100mm.
The drying process of paint film and putty film can be accurately measured by using circular track needle design, equipped with four different radius needle (R0.25/0.5/1.0/1 mm), and the track period is 24h/r.
Impact height of 120 cm, hammer mass 1000g, no secondary rebound phenomenon after impact, punch diaMeter 16mm, can accurately determine the impact strength of the paint film.
Adopt all directions swing vibration mode to ensure that the paint is fully mixed, Vibration Frequency 550 times/min, equipped with 0-15 minute timing function, suitable for 80-240mm barrel height range.
High-performance motor running smooth and low noise, with CPU digital display dynamic Rotation speed control, can realize timing fixed speed operation, Processing capacity 10-100L, lifting Travel 600mm, support a variety of mixing forms simple replacement.
The adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel ≥ 80mm. The integrity of the paint film was evaluated by seven grades, and the operation was simple and conformed to the GB/T1720 standard.
Using photo paper smooth surface combination technology, observing the imprint after applying a uniform load, the pressure range of the probe is 50-250N, and the diaMeter of the rubber probe is Φ 40mm, which can accurately evaluate the chalking grade of the paint film.
Konig and Persoz swing bars are used, Konig swing period is 1.4s, Persoz swing period is 1s, and the number of swing angles is automatically recorded, which is suitable for accurate determination of paint film Hardness.
Temperature sensitive discoloration paint after overheating Color from white to transparent, irreversible discoloration, suitable for rough oil surface, Measuring temperature 60 ℃, Net weight of plastic bottles 100 grams.
The pressure range of the probe is 50~ 250N, the diaMeter of the rubber probe is 40mm, and the degree of paint film chalking is evaluated by comparing the imprint of the photo paper with the standard sample, which is suitable for the detection of various environmental factors.
The equipment uses a spring lift system, lift Travel 200mm, speed range of 60~ 8000rpm, can adapt to different experimental needs, through the digital PID technology implementation High Accuracy control, and provide dispersed impeller and sand grinding disc.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0-10.5 mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Frequency of 710 vibrations per minute, mixing in 30 seconds; can handle 0.5 to 20 liters of barrel paint, equipped with safety interlock and height adjustment functions, quiet operation and easy loading.
Equipped with a 60mm diaMeter 304 stainless steel dispersion plate, it is corrosion-resistant and easy to clean; the lifting stroke is 11 to 42 centiMeters, which can be flexibly adapted to different containers; the handling capacity is up to 25 liters, meeting the needs of medium-scale experiments.