The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
It can measure the ability of the paint film to deform with the substrate without damage. It is equipped with a shaft Rod with a diaMeter of 50mm and 100mm.
The drying process of paint film and putty film can be accurately measured by using circular track needle design, equipped with four different radius needle (R0.25/0.5/1.0/1 mm), and the track period is 24h/r.
Impact height of 120 cm, hammer mass 1000g, no secondary rebound phenomenon after impact, punch diaMeter 16mm, can accurately determine the impact strength of the paint film.
Adopt all directions swing vibration mode to ensure that the paint is fully mixed, Vibration Frequency 550 times/min, equipped with 0-15 minute timing function, suitable for 80-240mm barrel height range.
Three rollers are used to crush each other to destroy the molecular binding force, and the material is crushed and mixed. The size of the roller is 65x135mm, the rotation speed of the middle roller is 88rpm, and the particle size of the starting material is 50~ 100μm.
The adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel ≥ 80mm. The integrity of the paint film was evaluated by seven grades, and the operation was simple and conformed to the GB/T1720 standard.
Using photo paper smooth surface combination technology, observing the imprint after applying a uniform load, the pressure range of the probe is 50-250N, and the diaMeter of the rubber probe is Φ 40mm, which can accurately evaluate the chalking grade of the paint film.
Konig and Persoz swing bars are used, Konig swing period is 1.4s, Persoz swing period is 1s, and the number of swing angles is automatically recorded, which is suitable for accurate determination of paint film Hardness.
Temperature sensitive discoloration paint after overheating Color from white to transparent, irreversible discoloration, suitable for rough oil surface, Measuring temperature 60 ℃, Net weight of plastic bottles 100 grams.
The pressure range of the probe is 50~ 250N, the diaMeter of the rubber probe is 40mm, and the degree of paint film chalking is evaluated by comparing the imprint of the photo paper with the standard sample, which is suitable for the detection of various environmental factors.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0-10.5 mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Frequency of 710 vibrations per minute, mixing in 30 seconds; can handle 0.5 to 20 liters of barrel paint, equipped with safety interlock and height adjustment functions, quiet operation and easy loading.
Using standard sand free fall brushing layer, straight grinding to expose 4mm substrate; can quantify the abrasion per unit thickness of the paint layer of sand volume, the inner diaMeter of the catheter 19mm, sample holder 45 degrees angle fixed.
Adopt horizontal three-roller extrusion grinding, roller clearance hand adjustment, maximum processing viscosity 3000000cps, roller can be cooled down water temperature control, fineness control precision, suitable for a variety of viscosity materials.