Using roll-to-roll continuous solution pool mode, the width of the substrate is 200mm, and it is dried by 130 ° C hot air Oven; the solution pool can be lifted and heated, and PLC control ensures stable operation, which is suitable for a variety of substrate processing.
Using a roll-to-roll continuous solution cell process, the substrate is crystallized or attached under specific conditions. Equipped with a 130 ° C hot air Oven drying system, the effective application width is 180mm, and the mechanical speed range is 0.1-300 mm/min. The solution cell has a lifting function and a separate heating design to ensure process Stability and operation safety.
Adopting double roll extrusion method, Spreader Film thickness range 0.3-10 mm adjustable, accuracy up to +/- 0.05mm, equipped with handwheel adjustment and dial indicator display, dip plate is 304 stainless steel material.
Adopting dip coating with double roll extrusion structure, Spreader thickness 0.3-10 mm adjustable, mechanical speed 1.2m/min can be slowly adjusted, built-in glue circulation system to ensure Spreader uniformity.
Using D type High Accuracy Impact device, Measurement range 30~ 110HS, can detect cast steel roll, forged steel roll and cast iron roll three kinds of hardness of materials, with anti-Impact and anti-electromagnetic interference ability, support 7 kinds of Hardness standard automatic conversion.
Using dip coating process with double roll extrusion residual material, Spreader thickness adjustable, mechanical speed 0.1-1 m/min, Oven temperature 50-150 ℃ +/- 3 ℃, suitable for a variety of Coating Spreader.
Adopt Cr12 steel roll, Hardness reaches HRC52 °~ 58 °, surface roughness 0.2~ 0.1, speed ratio 1:3:9, easy to operate and low noise, suitable for efficient grinding of various materials.
Using the immersion coating method, Spreader thickness 0.3-10 mm adjustable, mechanical speed 1.2m/min, built-in glue circulation system to ensure uniform and stable Spreader.
Laminating speed 1~ 10m/min, laminating accuracy 0.5mm, roll to roll Laminating design, equipped with automatic deviation correction device and split drying, suitable for a variety of non-elastic material Spreader.
Adopt double roll extrusion method to achieve 0.3-10 mm Spreader Film thickness, accuracy of +/- 0.05mm; Equipped with hot air circulation Oven, Temperature range room temperature to 200 ℃ +/- 3 ℃; Tension controller automatically controls the unwinding process to ensure the uniformity of Spreader.
Adopt Cr12 steel roll, Hardness reaches HRC52 °~ 58 °, Surface Hardness 0.2~ 0.1, easy to operate and easy to change color, suitable for fine grinding of material viscosity 30~ 8000cps range.
The Spin Coater is controlled by touch screen, the acceleration range is 100~ 4000rpm/s, and the speed can be automatically corrected by A/K selection. The motor torque is large and the operation is smooth, which is suitable for the assembly line process.
The three-roll extrusion grinding principle is adopted, the diaMeter of the roller is 65mm, the processing viscosity is 3 million cps, and the temperature can be controlled by chilling down water. The material of the roller can be selected from cemented carbide or zirconia ceramics.
The three-roll extrusion grinding principle is used to process materials with a viscosity of up to 3 million cps. The roller can control the temperature rise through chilled down water. The roller speed range is 23-178rpm. It supports the customization of ceramic materials such as zirconia and is suitable for paste grinding with high fineness requirements.
Micro-gravure plate coating method to achieve ultra-thin uniform coating, Spreader thickness range is wide; integrated online corona treatment makes the substrate surface tension up to 72dyne/cm; drying box temperature control accuracy +/- 3 ℃ to meet different solvent drying needs.