Adopt all directions swing vibration mode to ensure that the paint is fully mixed, Vibration Frequency 550 times/min, equipped with 0-15 minute timing function, suitable for 80-240mm barrel height range.
White part reflectance 80 +/- 2, non-Laminating design to enhance paint wettability, test area of 0.1 square Meters, Curl and checking resistance, suitable for brushing applications.
The equipment supports 0.5-20 liters of barrel paint mixing, revolution speed 100-200rpm, rotation speed 200-400rpm, using multi-stage intelligent frequency conversion speed regulation and door opening and shutdown protection to achieve smooth operation and safe operation.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Adopting rotary oscillation design, Frequency 3000rpm, pendulum amplitude 5mm, suitable for small containers such as testtube and Colorimetric tube, it can efficiently handle the experimental requirements of large chemical reactions and few solutions.
It can measure the ability of the paint film to deform with the substrate without damage. It is equipped with a shaft Rod with a diaMeter of 50mm and 100mm.
The drying process of paint film and putty film can be accurately measured by using circular track needle design, equipped with four different radius needle (R0.25/0.5/1.0/1 mm), and the track period is 24h/r.
Adopt 4mm small diaMeter design, suitable for surface or small area measurement; Repeatability Delta E * ab < 0.05 to ensure Measurement accuracy; Horizontal structure is small in size, comfortable and stable to hold.
Impact height of 120 cm, hammer mass 1000g, no secondary rebound phenomenon after impact, punch diaMeter 16mm, can accurately determine the impact strength of the paint film.
The tapered shaft size range is 3.2~ 38mm, and the shaft length is 203mm, which can test the cracking and disbonding performance of the paint film under bending conditions, in line with international standards.
The adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel ≥ 80mm. The integrity of the paint film was evaluated by seven grades, and the operation was simple and conformed to the GB/T1720 standard.
The eccentric spherical shaft design ensures uniform mixing, and the fixed speed of 2800RPM realizes fast vortex mixing. The TPU material countertop is wear-resistant and corrosion-resistant, small in size and low in noise.
Adopting stepless speed regulation technology with a maximum speed of 2800RPM, equipped with eccentric spherical shaft and wear-resistant TPU table, supporting two continuous operating Modes of point movement, the body is resistant to acid and alkali collision and has low operating noise.
Using photo paper smooth surface combination technology, observing the imprint after applying a uniform load, the pressure range of the probe is 50-250N, and the diaMeter of the rubber probe is Φ 40mm, which can accurately evaluate the chalking grade of the paint film.
32 5ml centrifuge tubes can be installed vertically on both sides, using a vertical installation design, suitable for HT-X100 swirl/spin Mixer, improving Sample Handling efficiency.