It can prepare a wet film thickness of 13.7 microns, with a wire-wound design providing stable coating performance. The 9.52 mm diaMeter ensures easy operation, making it suitable for various paint application scenarios.
Using the formed pRoduction process, Coating Weight is about twice that of the wire-wound coating Rod, wet film thickness is 13μm, film accuracy reaches 0.5 μm, and the material is 304 stainless steel.
Three rollers are used to crush each other to destroy the molecular binding force, and the material is crushed and mixed. The size of the roller is 65x135mm, the rotation speed of the middle roller is 88rpm, and the particle size of the starting material is 50~ 100μm.
Wet film thickness 45μm, main Rod diaMeter 10mm, effective application width 600mm, using SUS304 material, Coating Weight, length and surface preparation can be customized, suitable for a variety of Spreader conditions.
Wet film thickness 22.9 microns, diaMeter 9.52 mm, the forming Rod uses an extrusion process to process continuous grooves, with no wire breakage and easy cleaning; the wire-wound Rod is based on the traditional principle, and there are differences in coating amount.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0-10.5 mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
It can measure the ability of the paint film to deform with the substrate without damage. It is equipped with a shaft Rod with a diaMeter of 50mm and 100mm.
Using metal plating anilox roller, the number of lines can reach 180 lines/inch, which can precisely control the film fineness, and is suitable for the uniform Spreader test of inks Coating glue on various substrates.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Using the formed pRoduction process, the wet film thickness is 6 microns, the accuracy is 0.5 microns, the cleaning is convenient and there is no worry of broken wire, to ensure the precision and durability of the coating prepative.
The extrusion pRoduction process ensures uniform coating application, with a wet film thickness of 38.9 microns and a coating precision of up to 0.1 microns. The stainless steel material ensures long-lasting durability, making it suitable for a variety of coating testing needs.
Using 160 line metal anilox roller and rubber roller combination, print width 70mm, suitable for inks proofing, wet film thickness and the number of lines inversely proportional, proofing authenticity and easy to operate.
The photoelectric counter is used to realize automatic counting, and the measurement is fast and accurate; the period of M-3 swing Rod is 0.625s, and the swing time on standard Glass is 440 +/- 6s; the horizontal mechanism is improved, and the scale can be moved horizontally to facilitate zero adjustment.
Using 400 wire metal anilox roller to control the ink film thickness, flexographic samples can be quickly prepared, easy to use and clean, and the repRoducibility is very similar to that of conventional flexographic printing.
The bending diaMeter of putty film cracking peeling is tested by bending test plate, and the shaft Rod size is 50mm and 100mm. It is suitable for 0.2-0 mm thick tinplate substrate, and the operation is simple and reliable.