The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
The drying process of paint film and putty film can be accurately measured by using circular track needle design, equipped with four different radius needle (R0.25/0.5/1.0/1 mm), and the track period is 24h/r.
Hardness stainless steel material, Hardness 50~ 55HRC, accuracy up to +/- 2μm, with four film thickness optional, smooth surface wear and corrosion resistance, support custom specifications to meet different experimental needs.
Formed to achieve 52.6 micron precision film, 304 stainless steel material provides high Abrasion Resistance, 50mm at both ends of the hand part without additional handle, can be directly matched with the experimental Film Applicator.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0-10.5 mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Using imported wire Rod accuracy of 1 μ m, Spreader rate 5~ 200mm/s adjustable, support scraper and wire Rod two Spreader mode, Heating Temperature Uniformity +/- 3 ℃, suitable for a variety of substrate Film thickness treatment.
Coating speed 1~ 10m/min adjustable, wet film thickness range of 0.005-3mm, drying temperature up to 200 ℃, using continuous experimental film design, equipped with adjustable Blade Coating device and automatic deviation correction function.
Spreader thickness range 0.001-10mm adjustable, bar accuracy +/- 0.001mm, support 5-200mm/s stepless speed, through mechanical fixing and stable pressure to ensure film uniformity, improve experimental repRoducibility.
Impact height of 120 cm, hammer mass 1000g, no secondary rebound phenomenon after impact, punch diaMeter 16mm, can accurately determine the impact strength of the paint film.
Using 180 * 480mm size, with wire Rod or Film Applicator scraping ink, is conducive to the film flat and effective, improve film mass.
Adopting 500 * 700mm Dimensions, used with bar or Film Applicator, is conducive to the smooth and effective film, and improves the convenience of film operation.
The pressure range of the probe is 50~ 250N, the diaMeter of the rubber probe is 40mm, and the degree of paint film chalking is evaluated by comparing the imprint of the photo paper with the standard sample, which is suitable for the detection of various environmental factors.
It can measure the ability of the paint film to deform with the substrate without damage. It is equipped with a shaft Rod with a diaMeter of 50mm and 100mm.
Using a formed pRoduction process, the film thickness reaches 171.5 μm, and the stainless steel material ensures accuracy, which is suitable for experimental applications of different viscosity materials.
Spreader accuracy of +/- 0.003mm, thickness range of 0~ 10mm, speed 5~ 180mm/s adjustable, heating temperature to 180 ℃, using continuously variable speed and removable drawdown blade design, improve the convenience of operation and film conformity.