Using standard sand free fall brushing layer, straight grinding to expose 4mm substrate; can quantify the abrasion per unit thickness of the paint layer of sand volume, the inner diaMeter of the catheter 19mm, sample holder 45 degrees angle fixed.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Speed range 0-70rpm, equipped with a variety of load options and abrasive wheels of different materials to meet diverse testing needs, simple operation and stable performance.
The drying process of paint film and putty film can be accurately measured by using circular track needle design, equipped with four different radius needle (R0.25/0.5/1.0/1 mm), and the track period is 24h/r.
Double abrasive wheels swirl/spin friction design, adjustable friction load 500g to 1000g, working wheel Rotation speed 60rpm, to achieve non-directional abrasion, closer to the actual use of the scene.
Double abrasive wheels X-shaped friction track, friction non-directivity closer to the actual working conditions, working wheel Rotation speed 60rpm +/- 2rpm, friction load optional 500g to 1000g, equipped with automatic counting and grinding function.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0-10.5 mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Rotation speed is stable with stepper motor drive, working wheel Rotation speed 60/70rpm adjustable, equipped with different specifications abrasive wheels and turntable components, support multi-material wear test, avoid friction directional defects.
Impact height of 120 cm, hammer mass 1000g, no secondary rebound phenomenon after impact, punch diaMeter 16mm, can accurately determine the impact strength of the paint film.
The pressure range of the probe is 50~ 250N, the diaMeter of the rubber probe is 40mm, and the degree of paint film chalking is evaluated by comparing the imprint of the photo paper with the standard sample, which is suitable for the detection of various environmental factors.
It can measure the ability of the paint film to deform with the substrate without damage. It is equipped with a shaft Rod with a diaMeter of 50mm and 100mm.
Rotation speed is stable with stepper motor drive, working wheel Rotation speed 60/70rpm adjustable, supports two test configurations of paint film and wood, and the friction track is mesh to avoid directional defects.
Using photo paper smooth surface combination technology, observing the imprint after applying a uniform load, the pressure range of the probe is 50-250N, and the diaMeter of the rubber probe is Φ 40mm, which can accurately evaluate the chalking grade of the paint film.
With four film Film thickness, Spreader width 160mm, wear-resistant corrosion-resistant alloy steel material, can precisely control wet-film or dry-film thickness, ensure coating conformity and Repeatability.
With four film film thickness optional, Spreader width 160mm, wear-resistant corrosion-resistant alloy steel material, can precisely control wet-film or dry-film thickness, ensure coating conformity and Repeatability.