The adhesive force of the tape is 4.3N/cm, and the principle of cross-cut method is adopted, which is suitable for adhesion testing. The performance is stable and non-degumming, and the test results are accurate and reliable.
Using the formed pRoduction process, Coating Weight is about twice that of the wire-wound coating Rod, wet film thickness is 13μm, film accuracy reaches 0.5 μm, and the material is 304 stainless steel.
Equipped with 10-station synchronous test capability, 1000g weight and 1-999999 minute Timer, using SUS #304 steel plate to ensure test accuracy, and automatically recording tape peeling time.
Wet film thickness 22.9 microns, diaMeter 9.52 mm, the forming Rod uses an extrusion process to process continuous grooves, with no wire breakage and easy cleaning; the wire-wound Rod is based on the traditional principle, and there are differences in coating amount.
Using 2000g +/- 5g roller load and 300mm/min rolling speed to ensure that the adhesive tape sample is flat and evenly adhered to the standard substrate, in line with CNS-11888 and PSTC-8 design standards.
11/16 inch standard width paper tape, capable of completing approximately 1800 cycles of testing per roll, must be stored at 23 +/- 2 ° C and 50 +/- 10% Humidity to ensure Stability.
Using the formed pRoduction process, the wet film thickness is 6 microns, the accuracy is 0.5 microns, the cleaning is convenient and there is no worry of broken wire, to ensure the precision and durability of the coating prepative.
Support bar and Drawdown blade double coating method, suitable for high, medium and low viscosity materials; coating speed 1~ 300mm/s stepless adjustable, Blade Coating accuracy +/- 3μm; equipped with innovative clamshell magnetic Drawdown blade and simple bar installation, easy to clean and load; Heating and Vacuum chuck function to improve Spreader mass.
Adopt replica tape method to measure surface roughness, Peak Measurement range 20~ 115μm, accuracy +/- 5μm, with automatic subtracting substrate function, High Protection Rating, anti-solvent and water dust.
Wet film thickness 45μm, main Rod diaMeter 10mm, effective application width 600mm, using SUS304 material, Coating Weight, length and surface preparation can be customized, suitable for a variety of Spreader conditions.
Support bar and Drawdown blade two coating methods, suitable for different viscosity materials. Equipped with heating and Vacuum chuck function, servo motor to ensure stable operation. Drawdown blade film thickness control accuracy is high, uniform film.
Tack is good and non-degumming, adhesion reaches 7.6 N/cm, mass performance is stable, suitable for cross-cut adhesion testing, to ensure accurate film integrity assessment.
Employing an extrusion production process, the coating thickness is 105 microns, the coating width reaches 300 mm, and the coating accuracy can achieve 0.5 microns, ensuring coating uniformity and high-precision control.
Using SUS304 stainless steel material, wet film thickness 52μm, main Rod diaMeter 10mm, effective application width 600mm, groove design can achieve accurate Coating Weight control.
Measured value 500N, suitable for tape, PCB, adhesive tape and other materials disbonding force test, supporting the Force Gauge test bench.