A wet film with a film thickness of 50~ 675 μ m was prepared by using a coating scraper, and the sag property was observed when placed vertically. The maximum thickness without sag was expressed, which was suitable for Paints testing.
The multi-groove coating scraper can scrape 10 wet-films of different thicknesses at one time, the thickness difference of adjacent films is 25um, and the wide film thickness range of 50-675um is supported. It is convenient to visually observe the sag situation by placing the test plate vertically.
The stainless steel material ensures durability, the film thickness range is 450~ 675 μm, and the groove difference is 25 μm, which is convenient for accurate determination of Coating sag on site.
Dual function design can test leveling and sag at the same time, flow plane supports 5 kinds of film thickness Spreader, flow surface provides 10 kinds of film thickness range 75-300 micron, stainless steel material is acid and alkali resistant, in line with ASTM D4400 and D2801 standards.
Spreader 5 kinds of film thickness, the other side of the test sag cover 10 kinds of thickness 75-300 microns, stainless steel material acid and alkali resistance, in line with ASTM standards, easy to accurately evaluate film performance.
The device can pRoduce 10 different film thickness stripes, film thickness range 250-475μm, Graduation 25μm, suitable for vertical position testing, to help evaluate coating sag tendency and ensure stable test conditions.
Film thickness range 650~ 875 μ m, Graduation 25 μ m, stainless steel material, Dimension 120 * 22 * 20mm, suitable for the determination of relative sag of Paints.
The split structure is equipped with a dedicated thick coating Probe, Measurement range of 0~ 13000 μm, accuracy +/- 3%, IP65 Protection Rating and high-speed measurement capability of more than 60 readings per minute.
Made of stainless steel, the film thickness range is 250~ 475μm, Graduation 25μm, Dimension 120 * 22 * 20mm, suitable for standard sag performance testing.
Using eddy Current thickness measurement principle, equipped with ultra-thick coating special Probe, Measurement range 0~ 13000 μm, error +/- 3%, can read more than 180 data per minute, support 250,000 Measured value storage.
S136 stainless steel material, corrosion resistance and high Hardness; film thickness range 50-275μm, Spreader width 73.5mm, support multi-range optional, clear scale, easy to accurately determine Coating vertical flow performance.
The device provides 450-1000 μm film thickness test range, Graduation 50/100 μm, equipped with 10 grooves, can accurately simulate the vertical top coating film sagging behavior, ensuring stable and reliable test conditions.
Measuring wet-film flow thickening in the vertical state, controlling the physical performance of the coating to select the appropriate wet film thickness to ensure uniform film thickness, Film thickness range 450-675μm, in line with GB/T 9264 and ASTM D 3730 standards.
Scratch coating film thickness range of 50~ 275μm, groove difference of 25μm, stainless steel material, compact size of 120 * 22 * 20mm, suitable for the determination of Paints and other pRoducts.
Made of wear-resistant and corrosion-resistant alloy steel to ensure durability and accuracy, film Film thickness range 850~ 1075μm, adjacent film thickness difference of 25μm, suitable for vertical, corner, round hole, arc workpiece painting control.