Surface Water Absorbency was measured by Cobb test method, test area 100cm ² accuracy +/- 0.2cm ², liquid height 10mm, pressure roller mass 10kg to ensure uniform pressure, Cup body 316 stainless steel corrosion resistance.
The Water Absorbency of paper surface was measured by Cobb test method, the test area was 100cm ², the cylinder height was 50mm, the absorbent paper Basis Weight was 200~ 250g/m2, and the pressure roller mass was 10kg to ensure the accuracy of the test.
The surface water absorption of paper and Cardboard was measured by Cobb test method, the test area was 100 +/- 0.2cm ², and the mass of the pressing roller was 10 +/- 0.5kg. The water absorption value of Cobb can be accurately calculated.
Using the Cobb test method, the test area is 100cm ² +/- 0.2, and the pressure roller mass is 10kg +/- 0.5, which is suitable for the detection of Water Absorbency on the surface of sizing paper and Cardboard, and is not suitable for loose or unsizing paper.
The inner section area of the metal cylinder is 100 +/- 0.2cm ², and the test water consumption is 100mm +/- 5ml. It is suitable for the determination of Water Absorbency on the surface of sizing paper and Cardboard. The operation is simple and the results are accurate.
Test area of 100cm ², cylinder height of 50mm, can accurately determine the unit area of paper and Cardboard in the specified time surface absorption of water, using the Cobb test method for surface Water Absorbency test.
The Cobb test method is used to determine the water absorption value per unit area, the test area is 100cm ², the cylinder height is 50mm, and it is equipped with Basis Weight 200-250g/m2 absorbent paper, which meets the requirements of ISO535 and GB/T1540 standards.
It can quickly and accurately cut the standard sample with a diaMeter of 125mm, and the sampling thickness range is 0.1-0. It is suitable for the determination of paper Water Absorbency and is a special tool for the preparation of laboratory standard samples.
The Cobb test method was used to measure the water absorption per unit area, the cross-sectional area of the cylinder was 100 +/- 0.2cm ², and the Basis Weight of the absorbent paper was 200~ 250g/m2, which was suitable for the determination of the surface absorption weight of paper and Cardboard.
The test area is 100cm ² and the press roller mass is 10kg, which can accurately determine the Water Absorbency of the paper surface, and is suitable for the quality control and detection and analysis of the adhesive paper.
High Accuracy coaxial concentric structure is realized by three-point positioning method, the sampling error is +/- 0.2mm. The blade can be used for a long time after special treatment, and is suitable for materials with thickness of 0.1~ 1.5mm.
The three-point positioning guide structure and pure copper wear-resistant sleeve are used to ensure coaxial concentric accuracy; the service life of the special treatment die blade is up to 10 years; the sampling thickness range is 0.1~ 1.5mm, which meets the needs of various paper testing.
The stamping sampling structure is simple and firm, the knife edge is quenched, the sampling is labor-saving and accurate without burrs, the sampling thickness range is 0.1~ 1.0mm, and the sampling size error is 125mm +/- 0.2mm.
Using 100cm ² standard test area and 100ml test water, equipped with 10kg pressure roller to ensure uniform pressure of the sample, can accurately measure the liquid absorption in different time periods from 30s to 1800s, to meet a variety of test needs.
Sampling size Φ 125mm error +/- 0.2mm, thickness range 0.1~ 2.0mm, suitable for paper Cardboard surface water absorption weight detection, easy operation and high accuracy.