A wet film with a film thickness of 50~ 675 μ m was prepared by using a coating scraper, and the sag property was observed when placed vertically. The maximum thickness without sag was expressed, which was suitable for Paints testing.
The multi-groove coating scraper can scrape 10 wet-films of different thicknesses at one time, the thickness difference of adjacent films is 25um, and the wide film thickness range of 50-675um is supported. It is convenient to visually observe the sag situation by placing the test plate vertically.
Film thickness range 650~ 875 μ m, Graduation 25 μ m, stainless steel material, Dimension 120 * 22 * 20mm, suitable for the determination of relative sag of Paints.
Made of stainless steel, the film thickness range is 250~ 475μm, Graduation 25μm, Dimension 120 * 22 * 20mm, suitable for standard sag performance testing.
Spreader 5 kinds of film thickness, the other side of the test sag cover 10 kinds of thickness 75-300 microns, stainless steel material acid and alkali resistance, in line with ASTM standards, easy to accurately evaluate film performance.
Dual function design can test leveling and sag at the same time, flow plane supports 5 kinds of film thickness Spreader, flow surface provides 10 kinds of film thickness range 75-300 micron, stainless steel material is acid and alkali resistant, in line with ASTM D4400 and D2801 standards.
The stainless steel material ensures durability, the film thickness range is 450~ 675 μm, and the groove difference is 25 μm, which is convenient for accurate determination of Coating sag on site.
The device can pRoduce 10 different film thickness stripes, film thickness range 250-475μm, Graduation 25μm, suitable for vertical position testing, to help evaluate coating sag tendency and ensure stable test conditions.
Measuring wet-film flow thickening in the vertical state, controlling the physical performance of the coating to select the appropriate wet film thickness to ensure uniform film thickness, Film thickness range 450-675μm, in line with GB/T 9264 and ASTM D 3730 standards.
It can prepare a wet film thickness of 13.7 microns, with a wire-wound design providing stable coating performance. The 9.52 mm diaMeter ensures easy operation, making it suitable for various paint application scenarios.
Determination of wet-film flow thickening in the vertical state, control the physical performance of the coating to select the appropriate wet film thickness, film Film thickness 650-875 μ m, using high-quality wear-resistant corrosion-resistant alloy steel material to ensure durability and accuracy.
S136 stainless steel material, corrosion resistance and high Hardness; film thickness range 50-275μm, Spreader width 73.5mm, support multi-range optional, clear scale, easy to accurately determine Coating vertical flow performance.
S136 high grade stainless steel material, corrosion resistance and Hardness, film thickness range of 250~ 475μm, Spreader width of 73.5mm, suitable for a variety of ranges, clear and easy to read scale.
S136 high grade stainless steel material, corrosion resistance and Hardness, film thickness range 850~ 1075μm, Spreader width 73.5mm, multi-range optional, clear scale, suitable for vertical surface flowability and vertical flow performance evaluation.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.