The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0-10.5 mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
The drying process of paint film and putty film can be accurately measured by using circular track needle design, equipped with four different radius needle (R0.25/0.5/1.0/1 mm), and the track period is 24h/r.
It can prepare a wet film thickness of 13.7 microns, with a wire-wound design providing stable coating performance. The 9.52 mm diaMeter ensures easy operation, making it suitable for various paint application scenarios.
Impact height of 120 cm, hammer mass 1000g, no secondary rebound phenomenon after impact, punch diaMeter 16mm, can accurately determine the impact strength of the paint film.
The pressure range of the probe is 50~ 250N, the diaMeter of the rubber probe is 40mm, and the degree of paint film chalking is evaluated by comparing the imprint of the photo paper with the standard sample, which is suitable for the detection of various environmental factors.
It can measure the ability of the paint film to deform with the substrate without damage. It is equipped with a shaft Rod with a diaMeter of 50mm and 100mm.
Using photo paper smooth surface combination technology, observing the imprint after applying a uniform load, the pressure range of the probe is 50-250N, and the diaMeter of the rubber probe is Φ 40mm, which can accurately evaluate the chalking grade of the paint film.
Wound wire design, wet film thickness 125.7 microns, coating width 300 mm, stainless steel material ensures durability and precise coating effect.
Konig and Persoz swing bars are used, Konig swing period is 1.4s, Persoz swing period is 1s, and the number of swing angles is automatically recorded, which is suitable for accurate determination of paint film Hardness.
The 4-sided paint design can be prepared with four different thickness wet-film, application width 75mm, accuracy +/- 3μm, corrosion-resistant stainless steel material, easy to clean and durable.
Hand type easy to operate, load 1000g, standard 6B-6H pencil, suitable for film hardness testing, test temperature 23 +/- 2 ℃ and Humidity 50 +/- 5% environment.
Using standard sand free fall brushing layer, straight grinding to expose 4mm substrate; can quantify the abrasion per unit thickness of the paint layer of sand volume, the inner diaMeter of the catheter 19mm, sample holder 45 degrees angle fixed.
Using 200g weight and 1cm ² bottom area design, in line with GB/T 1728 standard, through the filter paper test method to accurately determine the film surface drying and practical drying time, easy to operate, reliable results.
The adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel ≥ 80mm. The integrity of the paint film was evaluated by seven grades, and the operation was simple and conformed to the GB/T1720 standard.