Adopt all directions swing vibration mode to ensure that the paint is fully mixed, Vibration Frequency 550 times/min, equipped with 0-15 minute timing function, suitable for 80-240mm barrel height range.
Adopt 0 ° illumination diffuse reflection reception principle, Repeatability ≤ 0.3, Indication Error +/- 1.0, suitable for white and shallow Paints hiding power measurement, easy and portable operation.
The equipment supports 0.5-20 liters of barrel paint mixing, revolution speed 100-200rpm, rotation speed 200-400rpm, using multi-stage intelligent frequency conversion speed regulation and door opening and shutdown protection to achieve smooth operation and safe operation.
Manual measurement of paint film Hardness, load 500g, test angle 45 °, can be inspected in any direction, three points contact with the measured surface.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Manual measurement of paint film Hardness, load 1000g, test angle 45 °, three-point contact with the tested surface design, suitable for inspection in any direction.
It can measure the ability of the paint film to deform with the substrate without damage. It is equipped with a shaft Rod with a diaMeter of 50mm and 100mm.
The drying process of paint film and putty film can be accurately measured by using circular track needle design, equipped with four different radius needle (R0.25/0.5/1.0/1 mm), and the track period is 24h/r.
Three-point contact design ensures 45 ° stability testing angle, equipped with 6B-6H pencil and 500g to 1000g adjustable load, manual push to achieve accurate film Hardness identification.
Impact height of 120 cm, hammer mass 1000g, no secondary rebound phenomenon after impact, punch diaMeter 16mm, can accurately determine the impact strength of the paint film.
The adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel ≥ 80mm. The integrity of the paint film was evaluated by seven grades, and the operation was simple and conformed to the GB/T1720 standard.
Using photo paper smooth surface combination technology, observing the imprint after applying a uniform load, the pressure range of the probe is 50-250N, and the diaMeter of the rubber probe is Φ 40mm, which can accurately evaluate the chalking grade of the paint film.
32 5ml centrifuge tubes can be installed vertically on both sides, using a vertical installation design, suitable for HT-X100 swirl/spin Mixer, improving Sample Handling efficiency.
Konig and Persoz swing bars are used, Konig swing period is 1.4s, Persoz swing period is 1s, and the number of swing angles is automatically recorded, which is suitable for accurate determination of paint film Hardness.
Temperature sensitive discoloration paint after overheating Color from white to transparent, irreversible discoloration, suitable for rough oil surface, Measuring temperature 60 ℃, Net weight of plastic bottles 100 grams.