The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0-10.5 mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Rotation speed 80rpm, Working Travel 80mm, in line with international standards, to ensure accurate and reliable film adhesion assessment.
The adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel ≥ 80mm. The integrity of the paint film was evaluated by seven grades, and the operation was simple and conformed to the GB/T1720 standard.
Electric Circle-drawing is used to ensure uniform speed and constant strength, Travel 20-80mm adjustable, Rotation speed 10-120 +/- 1 rpm adjustable, equipped with automatic judgment prompts and precision dual rail system to improve test Repeatability and data accuracy.
Hand type easy to operate, load 1000g, standard 6B-6H pencil, suitable for film hardness testing, test temperature 23 +/- 2 ℃ and Humidity 50 +/- 5% environment.
The drying process of paint film and putty film can be accurately measured by using circular track needle design, equipped with four different radius needle (R0.25/0.5/1.0/1 mm), and the track period is 24h/r.
Using 200g weight and 1cm ² bottom area design, in line with GB/T 1728 standard, through the filter paper test method to accurately determine the film surface drying and practical drying time, easy to operate, reliable results.
Impact height of 120 cm, hammer mass 1000g, no secondary rebound phenomenon after impact, punch diaMeter 16mm, can accurately determine the impact strength of the paint film.
The pressure range of the probe is 50~ 250N, the diaMeter of the rubber probe is 40mm, and the degree of paint film chalking is evaluated by comparing the imprint of the photo paper with the standard sample, which is suitable for the detection of various environmental factors.
It can measure the ability of the paint film to deform with the substrate without damage. It is equipped with a shaft Rod with a diaMeter of 50mm and 100mm.
Adopt the circular roller scratch method to evaluate the adhesion grade, describe the adjustable diaMeter of 0-10.5 mm, equipped with four weights to achieve 200-1000g loading, table Travel ≥ 80mm, manual operation is stable and reliable.
Three-point contact design ensures 45 ° stability testing angle, equipped with 6B-6H pencil and 500g to 1000g adjustable load, manual push to achieve accurate film Hardness identification.
Using photo paper smooth surface combination technology, observing the imprint after applying a uniform load, the pressure range of the probe is 50-250N, and the diaMeter of the rubber probe is Φ 40mm, which can accurately evaluate the chalking grade of the paint film.
Konig and Persoz swing bars are used, Konig swing period is 1.4s, Persoz swing period is 1s, and the number of swing angles is automatically recorded, which is suitable for accurate determination of paint film Hardness.