Measurement principle using ultrasonic, Measurement range 13~ 1000μm, accuracy +/- (2μm + 3%), suitable for wood, plastic and other substrates polymer Coating thickness detection.
With paint penetration measurement ability, accurate measurement of wall thickness without removing coatings, thickness range 2.5~ 125mm, accuracy +/- 0.03mm, support multi-echo and single-echo mode switching, suitable for detection needs of different surface conditions.
Hand type easy to operate, load 1000g, standard 6B-6H pencil, suitable for film hardness testing, test temperature 23 +/- 2 ℃ and Humidity 50 +/- 5% environment.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0~ 10.5mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
Impact block weight 500 +/- 5g, ball diaMeter φ 14 Hardness HRc60-66, can accurately assess the damage grade of paint film.
Frequency 5.0MHz, support paint layer detection and emission to echo mode, Measurement range 2~ 160mm, suitable for a variety of workpiece thickness measurement.
The drying process of paint film and putty film can be accurately measured by using circular track needle design, equipped with four different radius needle (R0.25/0.5/1.0/1 mm), and the track period is 24h/r.
Impact height 40cm, drop weight mass 500g, the degree of damage to the paint film is assessed by steel ball Impact, and the digital grade shows the anti-Impact ability, which is suitable for standard testing.
Set cross-cut adhesion, film thickness and Buchholz Crowd Hardness three test functions in one, cross-cut knife 6 blade spacing 1mm/2mm, Crowd knife load 500 +/- 5g, using the destruction Measurement principle.
In line with ISO2808-1974 standard, the range is 0~ 150μm, the accuracy is not more than 5μm, can measure the wet film thickness and estimate dry-film thickness, suitable for laboratory and pRoduction control.
Sharp probe measurement without leaving marks, measurement range 6%~ 90%, support wood moisture content and wood humidity equivalent value display, equipped with extended Probe and hammer ElectRode for different depth measurement.
It can prepare a wet film thickness of 13.7 microns, with a wire-wound design providing stable coating performance. The 9.52 mm diaMeter ensures easy operation, making it suitable for various paint application scenarios.
Mechanical design for measurement on any surface, using hardened stainless steel, measurement disc diaMeter 50mm, thickness 11mm, equipped with aluminum free swirl/spin rollers, reading accuracy +/- 2μm.
The paint film adhesion was measured by the circular trace method, the drawing diaMeter was 0-10.5 mm, and the Working Travel was 80mm. The integrity of the paint film was evaluated according to seven grades, and the operation was simple and reliable.
In line with ISO2808 standard, the range is 0~ 500μm, the accuracy is not more than 5μm, can measure the wet film thickness and estimate dry-film thickness, suitable for laboratory and pRoduction site.