Impact specimens with semi-spherical punches are used for energy consumption measurement to evaluate anti-Impact performance. Impact energy range is 3J, Impact speed is 2.5m/s, and it is suitable for a variety of film and paper tests.
Equipped with 200 +/- 0.2g Koenig pendulum and 500g platinum saz pendulum two configurations, the swing period is 1.4 +/- 0.02s and 1 +/- 0.001S, through the photoelectric system automatic measurement of film damping time, to meet the different standards of test requirements.
Impact energy 2.7mJ, Impact device mass 75g, small damage to the measured surface, does not damage the hardened layer, suitable for measurement of small and thin parts, the minimum thickness of the specimen is 1mm, and the minimum depth of the hardened layer is 0.2mm.
Adopting Koenig pendulum structure, the total mass is 200 +/- 0.2g, and the swing period is 1.4 +/- 0.02s. The coating Hardness is accurately measured by the swing attenuation time, and the number of swing angles is automatically recorded.
Impact energy 3N, Impact device mass 75g, suitable for measurement of small or thin specimens and surface hardening layer, the minimum thickness can be measured 1mm and the minimum hardening layer depth 0.2mm.
Using electromagnet cissing pendulum, equipped with two laser Probe recording data, can test 0.1mm to 5.5mm thickness test plate, swing period 1.4s, Organic Glass door cover to reduce the impact of airflow.
Impact height up to 120 cm, weight weight mass 1000g, no secondary rebound after impact, to ensure accurate and reliable test results, suitable for film impact performance evaluation.
Equipped with 200 +/- 0.2g and 500 +/- 0.1g two swing bars, can measure the film damping time, reflect the surface Hardness through swing attenuation, support different standard test requirements.
Impact height 0-50cm can be accurately adjusted, drop weight mass 1000g with the Φ 8mm punch, can accurately determine the film anti-Impact performance, easy to operate and Repeatability.
Impact height of 120 cm, hammer mass 1000g, no secondary rebound phenomenon after impact, punch diaMeter 16mm, can accurately determine the impact strength of the paint film.
Using stopwatch counting method, the length of the swing Rod is 500 +/- 1mm, and the total mass of the swing is 120 +/- 1g. The resistance to deformation is evaluated by measuring the ratio of the swing amplitude time on the film to the swing time on the Glass.
Impact energy is only 2.7mJ, minimal damage to the measured surface, does not damage the hardened layer, suitable for testing 1mm thickness of small parts, Cedar diaMeter minimum 0.32mm.
Impact height 120 cm, drop weight mass 1000g, punch diaMeter Φ 16mm, Impact depth 2.5mm, no secondary rebound phenomenon, to ensure the accuracy of the test.
Impact height of 120 cm and 1000 g hammer mass, anti-springback design, punch diaMeter of 16 mm, can accurately determine the film resistance to rapid deformation.
Impact height 0-50cm adjustable, equipped with 1000g drop weight and Φ 8mm punch, Impact depth 2mm, can accurately determine the material resistance to Impact performance.